Weld crack
Weld crack 1.1. Cracking: If a weld crack is found, it must be removed and magnetic-particle inspection performed to ensure every point has been removed before re-welding. Weld Crack can occur on top of a weld…
blogs
Dissimilar metal in TIG Welding process
Why use this TIG welding process: TIG Tungsten Inert Gas otherwise called as GTAW- Gas Tungsten Arc Welding , Involves melting the metal using the arc created by tungsten electrode, The welding can be done with or without filler metal, Argon Gas is used as shielding around…
blogs
NDT Methods Selection
NDT Method Selection: The NDT (nondestructive testing) methods are: Visual Inspection – VT Liquid Penetrant Testing – LT Magnetic Particle Testing – MT Radiographic Testing – RT Ultrasonic Testing – UT Eddy Current Testing – ET (not used in field inspection) Acoustic Emission Testing –…
blogs
Weld Test Coupon Preparation
Bend Test Coupon Preparation First the centerline on the plate shall be marked. Then another line 1.0 inch above the center line and another line 1 inch below the center line. This is the section that can be used as an alternate coupon in the event…
blogs
Non Destructive Testing- Course and NDT course Fee
Non Destructive Testing has plenty of scope for people interested in Mechanical Industry and also construction sector. This Quality Control Related subjects is thought in almost all major cities all over the world, and the NDT certificates offered by institutes are valuable across the globe. The…
blogs
Weld defects
Failure investigation often uncovers facts that lead to changes in design, manufacturing, or operating practice, which will eliminate similar failures in the future. Failures of insignificant parts can also lead to advances in knowledge and should be done objectively, as with a large structure. The…
blogs
Adhesion Test on Paints by Tape Test
Painting Inspection, Adhesion Test, QC Training, QC Course X Cut Test (This Document) Cross Cut Tape Test Method A – X Cut Tape Test An X-Cut is made on the Dry Paint until the bare substrate , a…
blogs
Concepts of Welding Defects and Discontinuities
Welding defects can be classified as structural discontinuities and consist of: porosity, slag inclusions, lack of fusion, cracks, etc. Porosity is gas pockets or voids in the weld metal which are free of any solid materials, such as It is formed as a result…